| Authors | پوریا گمرکچی,مریم غیاثیان آرانی,Elmuez A. Dawi,Aseel M. Aljeboree,Forat H. Alsultany,مهدی شبانی نوش آبادی,مسعود صلواتی |
|---|
| Journal | Energy Nexus |
|---|
| Page number | 100597 |
|---|
| Volume number | 20 |
|---|
| IF | 9.5 |
|---|
| Paper Type | Full Paper |
|---|
| Published At | 2025-11-18 |
|---|
| Journal Grade | Scientific - research |
|---|
| Journal Type | Electronic |
|---|
| Journal Country | Iran, Islamic Republic Of |
|---|
| Journal Index | ISI-Listed ,SCOPUS |
|---|
| Keywords | Manganese vanadate nanostructuresPhase purityMorphologyElectrochemical hydrogen storageHydrothermal |
|---|
Abstract
Hydrothermal manufacturing of manganese vanadate nanostructures in the presence of ligand as capping agent which employed as electrode materials with custom form was achieved. Different settings produced samples with different content, phase purity and shape. Structural properties investigated by XRD, FT-IR, EDX, FE-SEM, TEM and BET. Activity of electrode materials with various phase purities was compared using the charge-discharge test. The manufactured Mn(VO3)2 (MV2) shows a capacity of 507 mAhg-1 after 20 cycles at a current density of 1 mA. Other synthesized samples MV3 and MV4 with phase content of Mn2V2O7 and Mn(VO3)2 represents capacity in maximum level (20th cycle) 250 and 435 mAhg-1, respectively. So, sample MV2 shows higher electrochemical hydrogen storage capacity which synthesized by assembling nanoparticles to form of small sheets.