Synthesis and Thermoluminescence of ZnS:Mn2+ Nanoparticles

چکیده مقاله

The controlled chemical method has been used for synthesis of Mn doped ZnS nanoparticles. Optical absorption studies showed that increasing of surfactant density, from 0.0001 to 0.5 mol/lit., causes the size of nanoparticles to decrease from 4.8 nm to about 3 nm and the band gap width to increase from 4.15 to 4.50 eV. Also increasing the temperature during the synthesis process caused the nanoparticle size to be increased. As a new result we observed a thermoluminescence (TL) glow peak at about 475 K, with its intensity depending on concentration of the Mn dopant. Activation energy of this glow peak was obtained to be about 0.6eV. A discussion of the obtained results is also presented.